Bu çalışmada hidrojen peroksit ve demir kaplı zeolitle katalitik ozonlama ile humik asit giderimi incelenmiştir. Sonuçlar çözünmüş
organik karbon (ÇOK), UV254, SUVA254 (254 nm'de (spesifik Ultraviyole absorbansı) ve renk absorbansı (A436) parametreleri
ölçülerek değerlendirilmiştir. 60 dakikada pH 6.5'da 10 mg/L ozon konsantrasyonunda yalnız başına ozonlama ile %21,4 ÇOK
giderimi elde edilirken demir kaplı zeolitle (0,75 mg/L) katalitik ozonlama deneylerinde %62 ÇOK giderimi elde edilmiş, katalitik
ozonlama sistemine 1 mg/L hidrojen peroksit ilavesiyle de (%64,6 ile ) çok hafif bir artış gözlenmiştir. katalitik ozonlama yalnız
başına ozonlamaya kıyasla UV absorplayan aromatik yapının parçalanmasına katkıda bulunmuş ve ÇOK giderimini de
iyileştirmiştir ancak katalitik ozonlama sistemlerinde ozon konsantrasyonunun artışı giderim veriminde kayda değer bir artış
sağlamamıştır.
This study examined the catalytic ozonation of humic acid (HA) with iron coated zeolite (ICZ) and hydrogen peroxide (H2O2). The
results were evaluated by DOC that specify organic matter, UV254, SUVA254 (Specific Ultraviole Absorbance at 254 nm), and A436.
When ozonation was used alone, DOC removal was obtained as 21.4% at ozone concentration of 10 mg/L, pH 6.50 and oxidation
time of 60 min. DOC removal was found to increase by the the addition of H2O2 in ozonation process. The use of ICZ as catalyst
increased the decomposition of humic acid compared to ozonation alone. DOC removal efficiency was obtained as 62.0% at pH 6.5,
at catalyst loading of 0.75 g/L, and oxidation time of 60 min. In catalytic ozonation process DOC removal slightly incresed, when
H2O2 was added. 64.6% DOC removal was obtained at ozone concentration of 10 mg/L, catalyst dosage of 0.75mg/L and H2O2
concentration of 1 mg/L. The catalytic ozonation enhanced the destruction of the aromatic and UV-absorbing structures compared
with ozonation alone. However, increasing ozone concentrations did not increase removal efficiencies significantly in the catalytic
ozonation processes.